Cause Analysis of Damaged Refractory Material of Submerged Arc Furnace Lining

What is the main reason for the damage to the refractory material of the submerged arc furnace lining? Today, Luoyang Quantong Kiln Industry Co., Ltd. will take you to understand:

1. The penetration of molten iron destroys the penetration of molten iron into the carbon brick along the pores of the carbon brick. The infiltrated molten iron dissolves the binder in the carbon brick, and then dissolves the carbon particles in the carbon brick, destroys the compactness of the carbon brick, and reduces the carbon brick. The molten iron infiltrated into the carbon brick reacts with the carbon brick to form a brittle substance like FexC. The hot surface of the carbon brick forms an embrittlement layer.

2, the circulation of molten iron in the furnace

The circulation of molten iron aggravates the erosion and erosion of the brittle layer on the surface of the carbon brick by molten iron, which makes the carbon brick thinner. The bricks are strongly eroded by the flowing slag iron, thereby reducing the life of the furnace lining.

3. Corrosion of carbon bricks by alkali metals and zinc

Thermodynamic calculations show that when the heat transfer performance of the carbon brick is poor, there is a large temperature difference between the hot surface and the cold surface, and the thermal stress of the temperature difference inside the carbon brick is large, which induces cracks in the carbon brick, and pure alkali metal vapor passes through the carbon brick. The microcracks of the carbon bricks continuously flow and spread to the low temperature area of ​​the carbon brick, and the microcracks are the cause of the ring cracks. If the alkali metal vapor enters the microcracks of the carbon brick, when the temperature reaches 800 degrees Celsius, the alkali metal vapor will be in the microcracks. liquefaction, and then react with the silica-alumina ash of carbon bricks, causing the volume of ash to expand by 30%, aggravating the expansion of microcracks in carbon bricks and forming cracks. Activated carbon deposits are formed in the cracks. This reaction continues, the carbon brick cracks are continuously expanded and squeezed, the carbon brick cracks continue to expand, and finally the carbon bricks are split to form ring cracks. Improving the thermal conductivity of carbon bricks can prevent ring cracks. effective means